Avaliação da resistência mecânica em compósitos de argamassa com adição de pó de vidro após exposição a elevadas temperaturas

Show simple item record

dc.contributor.advisor Simon, Douglas Alexandre pt_BR
dc.contributor.author Moser, Nivaldo José pt_BR
dc.date.accessioned 2021-02-25T23:48:56Z pt_BR
dc.date.available 2021-02-25T23:48:56Z pt_BR
dc.date.issued 2019 pt_BR
dc.identifier.uri https://dspace.ifrs.edu.br/xmlui/handle/123456789/220 pt_BR
dc.description.abstract Concretos e argamassas, amplamente empregados na construção civil, oferecem grande resistência mecânica na temperatura ambiente. Porém, ao serem submetidos a elevadas temperaturas, como no caso de incêndio, perdem essas propriedades devido à remoção da água estrutural dos silicatos na matriz de cimento. O objetivo principal desse trabalho é avaliar a resistência mecânica de compósitos constituídos de argamassa e pó de vidro, com 28 dias de cura e após exposição a elevadas temperaturas. Foi estabelecida uma argamassa sem vidro como padrão de referência e outras três formulações contendo pó de vidro. As proporções de cimento e cal hidratada foram mantidas em todas as formulações. A formulação com pouco vidro foi constituída por 1,2 volumes de pó de vidro para 4,8 volumes de areia, enquanto a formulação com mais vidro teve três volumes de cada e outra somente com pó de vidro como agregado. Após exposição a elevadas temperaturas, 800, 1000 e 1200 °C, os corpos de prova contendo 20% de vidro, apresentaram resistência mecânica e integridade física, enquanto que o mesmo não foi observado para o padrão de referência. Esses resultados demonstraram a viabilidade potencial do pó de vidro para o desenvolvimento de uma argamassa resistente a elevadas temperaturas. pt_BR
dc.description.abstract Concrete and mortar widely used in construction offer great mechanical resistance at room temperature. However, when subjected to high temperatures as in the case of fire they lose these properties due to the removal of structural water from silicates in the cement matrix. The main objective of this work is to evaluate the mechanical strength of composites composed of mortar and glass powder with 28 days of cure and after exposure to high temperatures. A mortar without glass was established as a reference standard and three other formulations containing glass powder. The proportions of cement and hydrated lime were maintained in all formulations. The low-glass formulation consisted of 1.2 volumes of glass powder to 4.8 volumes of sand while the more-glass formulation had three volumes each and one with only glass powder as an aggregate. After exposure to high temperatures, 800, 1000 and 1200 °C, specimens containing 20% glass powder showed mechanical resistance and physical integrity while, it was not observed for the reference standard. These results demonstrated the potential viability of glass powder for the development of a high temperature resistant mortar. en
dc.format.mimetype application/pdf pt_BR
dc.language.iso por pt_BR
dc.rights Open Access en
dc.subject Resistência de materiais pt_BR
dc.subject Materiais compostos pt_BR
dc.subject Vidro pt_BR
dc.title Avaliação da resistência mecânica em compósitos de argamassa com adição de pó de vidro após exposição a elevadas temperaturas pt_BR
dc.type Dissertação pt_BR
dc.degree.grantor Instituto Federal de Educação, Ciência e Tecnologia do Rio Grande do Sul pt_BR
dc.degree.level Mestrado pt_BR
dc.degree.date 2019 pt_BR
dc.degree.local Farroupilha, BR-RS pt_BR
dc.degree.program Programa de Pós-Graduação em Tecnologia e Engenharia de Materiais pt_BR
dc.degree.department Campus Farroupilha pt_BR


Files in this item

Files Size Format View Description
123456789220.pdf 2.021Mb PDF View/Open Texto completo

This item appears in the following Collection(s)

Show simple item record

Search DSpace


Advanced Search

Browse

My Account